Model NO.: XGPF1201
Width: 1.5D
Function: High Strength Fiber
Structure: Miscellaneous Chain Synthetic
Model: Xgpf1201
Colors: Yellowish
Fiber: PARA-Aramid
Density: 1.47g/cm3
P-Aramid Content: 100%
Average Fiber Length: 1mm
Tensile Strength: 19.4-21 Cn/Dtex
Tensile Modulus: 80gpa~120gpa
Elongation at Break: 2.5%-3.84%
Moisture: <0.2%
Trademark: XIANGU
Transport Package: 5kg Per Bag
Specification: ROHS
Origin: Guangdong
HS Code: 54021190
1mm friction material aramid chopped strands was chopped in 1mm by a special cutting equipment. This fiber has high strength and modulus, strong hydrogen bonding strength, strength up to 28 g/d or more, strength is 5-6 times of steel wire.specific modulus 2-3 times of it,toughness 2 times of it while weight is just 1/5 of the wire.Continuous using temperature range is extremely wide, long running in the range of -196 ºC to 204 ºC,no decomposition and melting at high temperature of 560 ºC,strength can maintain 75% through 100 hours at 200 ºC.also has good chemical solvent resistance, resisting acid and alkali, anti-aging, good adhesion to rubber. Usually it is used as a reinforcing material in the fields of thermoplastics, thermosetting plastics, high-temperature composite structures, brake pads, clutch linings, friction material, wear-resistant filler, cable sheathing, gaskets, slot insulation, phase insulation barrier, interturn insulation and so on.
Â
SPECIFICATIONS:
| Model: |
XGPF1201 |
| Color: |
yellowish |
| Fiber type: |
Para-aramid |
| Density(g/cc) |
1.47 |
| Linear density of mono filament(D) |
1.5 |
| Filament diameter(μm) |
12 |
| Fiber length(mm) |
1 |
| Tensile strength( cN/dtex) |
19.4-21 |
| Elongation at break(%) |
2.5-3.84 |
| Tensile modulus(GPa) |
80~120 |
| Shrinkage(%) |
<0.2(190ºC×15m) |
| Moisture (%): |
<0.2 |
APPLICATION FIELDS:
1.Engineering Plastics,thermosetting resin,friction materials, automotive brakes,composite materials and Kevlar reinforced paper.Â
2.reinforcing materials,construction,rubber,reinforced cable,cable and other high-intensity rope.
3.composite material with resin or rubber,can significantly reduce the weight,increase loading weight,suitable for the production of aerospace equipment,high-speed trains and yachts shell.
4.Friction and sealing materials,friction materials reinforced fiber, significantly improved wear resistance,suitable for high temperature conditions.
Â
STORAGE:
The 1mm friction material aramid chopped strands should be keep dry in their original bags and stored in a suitable place,preferably at room temperature with 35-65% relative humidity.Avoid the sun, rain and fire
PACKAGING:
1.Inner black plastic film bags,net weight 5.00kg.gross weight 5.20kg.
2.Bag size:43*36*28cm,net weight 120.00kg.gross weight 150.00kg.
SHIPMENT AND TRANSPORTATION:
1.Shipment by sea:for sea transportation,generally 20 pallets(each 180kg.two layers)be loaded into 20 feet container.total net weight is 2400kg.
Carbon fiber fabric
Carbon fiber fabric is a type of textile material that is made from carbon fibers. It is known for its high strength-to-weight ratio, making it incredibly lightweight yet strong. The fabric is woven from carbon fibers, which are thin strands of carbon atoms that are highly durable and stiff.
Carbon Fiber Bi-Direction Fabric,Carbon Fibre Cloth Roll,Carbon Fiber Bidirectional Fabric,Fire Resistant Carbon Fiber Fabric
Jiangyin Phecda New Material Technology Co., Ltd , https://www.jiangyinphecda.com